National Institute Of Materials Physics - Romania

Bioactive glasses (BGs) are known for their selective ability to (i) form a mechanically strong interfacial bond with hard (bone) or soft tissues (gingivae or cartilages) (i.e., silica-, silica-phosphate-, phosphate-, boratephosphate-, or silica-phosphate-borate-based BGs); or (ii) serve as reservoirs for fast-release of therapeutic (osteogenic, angiogenic, anticarcinogenic, or antimicrobial) ions (i.e., phosphate-based BGs and mesoporous BGs). The strength of the bone bond yielded by the osteoproductive-capable BGs is generally equivalent to, or higher than the bone strength. The resorbability of phosphate-based BG is dependent on the content of network formers and cross-linkers. All BGs elicit excellent biochemical compatibility. However, their fracture toughness is typically less than and the elastic modulus is greater than those of bone, indicating that most BGs have suboptimal biomechanical compatibility when used in load-bearing applications. One promising approach to overcome this problem is the development of BGs in coating form, applied to the surface of load-bearing endosseous implants. This work critically assesses BG thin-layers fabricated by the radio-frequency magnetron sputtering method, an industry-ready large-scale physical vapour deposition technology. It is demonstrated that, despite the relative lack of attention paid to this technology, it enables the development of unique BG coatings with efficacious therapeutic capabilities. Here, we present an overview of the most relevant developments achieved thus far, along with the remarkable advantages, drawbacks to overcome, and future perspectives with the intention of highlighting the vast possibilities of this specific field of research.

Present work reports a systematic study on the evaluation of magnetic inhomogeneities in non-stoichiometric Mg0 & sdot;5Ca0 & sdot;5Fe2O4 nanoferrite (MCNF) by conducting exhaustive dc -magnetization, ac -susceptibility and Fe-57 Mossbauer spectroscopic measurements and exchange bias investigations using training protocol down to 6 K. Rietveld fitting to PXRD established the formation of anticipated spinel fcc phase of MCNF (non-stoichiometric) along with a minute impurity phase of calcite. Scherrer method and HRTEM micrographs illustrated broad size distribution of MCNF nanoparticles with an average nanocrystallite size of -15 nm. Combined 57Fe Mo center dot ssbauer spectroscopic and dc -magnetization analysis establishes coexistence of ferrimagnetic (67 %) & superparamagnetic (33 %) states at 300 K with notable M-s = 22 emu/g, M-r = 4 emu/g & H-c = 130 Oe and blocking of most of the nanoparticles of MCNF below 300 K. The coercivity followed the size -modified Kneller law for ferrimagnetic nanoparticles and the saturation magnetization abides the Bloch law. Moreover the frequencydependent ac -susceptibility investigations revealed two magnetic transitions: (i) A transition at - 330 K in the low frequency data attributed to the relaxation of blocked particles of bigger sizes under the superparamagnetic (SPM) regime and (ii) an irregularity at low temperatures is assigned to surface spin glass freezing. Surface spin glass freezing was further affirmed by the ageing experiments and dynamic scaling law. Furthermore, even the best fit to the dynamic scaling couldn't assert the existence of conventional spin glass phase due to slower spin -flip time of surface spins. A soft ferrimagnetic core of MCNF is enveloped with disordered surface spins, which manifest spin glass state. Concurrently, the findings of exchange bias at 30 K and training effect at 6 K affirmed that MCNF nanoparticles are presenting themselves as FM core- SG shell system. Our experimental findings suggested magnetic inhomogeneities comprised of superparamagnetism, ferrimagnetism and disordered surface spin glass state in the non-stoichiometric MCNF.

In a milestone paper [F. D. M. Haldane, Phys. Rev. Lett. 61, 2015 (1988)], Haldane elaborated a model of graphene within the time -reversal symmetry breaking is achieved by next -nearest -neighbors imaginary counterrotating hopping, hence conferring topological properties. In recent years, the time -reversal symmetry turned out to be broken also by light irradiation in so-called Floquet topological insulators (FTIs). On the other hand, Kane and Mele introduced a spin -orbit coupling (SOC) model [C. L. Kane et al., Phys. Rev. Lett. 95, 226801 (2005)] inspired by the Haldane's mechanism. In this paper, we present the topological properties of a FTI possessing SOC, using graphene as the playground. It was found that the interplay between sublattice subspace and the spin one triggers interesting topological phase transitions. Basically, in a FTI with SOC, two topological phases may be excited: charge quantum Hall effect (CQHE) and, respectively, spin quantum Hall effect (SQHE) phases. Also, it was demonstrated that the CQHE and SQHE coexistence is forbidden by the topology of the system. As well, it was identified a special driving regime of spin filter (SF), in which only one spin state is topological and, consequently, will be filtered in quantum transport.

This work describes the development of a flexible uric acid (UA) biosensor based on palladium-coated submicrometer electrospun poly(methylmethacrylate) (PMMA) fibers metalized with gold and attached to polyethylene terephthalate substrate (Pd/Au/PMMA/PET). The morphological characterization conducted by scanning electron microscopy revealed nanoscale Pd dendritic structures. Electrochemical investigations in the absence and in the presence of redox probes demonstrated that these Pd nanostructures are responsible for a six-fold increase in the electroactive area and enhanced electron transfer kinetics when compared to the gold-coated electrospun fibers. The UA biosensor obtained by immobilizing the uricase enzyme (UrOx) onto the Pd/Au/PMMA/PET electrode surface, allowed UA detection with a sensitivity of 431 mu A cm(-2) mM(-1) and a limit of detection of 12 mu M. Investigation of the redox reactions of hydrogen peroxide (a product of the enzymatic oxidation of UA by UrOx) at the Pd/Au/PMMA/PET electrode demonstrated that the working principle of the biosensor is based on the reduction of PdO produced at the electrode surface during the spontaneous reduction of hydrogen peroxide on Pd. This allows a biosensor operating potential of -0.05 V (vs Ag/AgCl) with high selectivity. The UrOx/Pd/Au/PMMA/PET biosensor was applied for UA detection in body fluids (sweat, urine, and blood serum) with recovery values between 98 and 105%, which were validated by high-performance liquid chromatography analysis. The stability of the device was evaluated over a period of 3 months, retaining 78% of the initial sensitivity, and reproducibility with RSD = 4.9% was achieved. The analytical performance of the biosensor under harsh mechanical deformations and at physiological temperatures demonstrated the potential applications of the device to wearable sensing platforms.

SiGeSn nanocrystals (NCs) in oxides are of considerable interest for photo-effect applications due to the fine-tuning of the optical bandgap by quantum confinement in NCs. We present a detailed study regarding the silicon germanium tin (SiGeSn) NCs embedded in a nanocrystalline hafnium oxide (HfO2) matrix fabricated by using magnetron co-sputtering deposition at room temperature and rapid thermal annealing (RTA). The NCs were formed at temperatures in the range of 500-800 degrees C. RTA was performed to obtain SiGeSn NCs with surfaces passivated by the embedding HfO2 matrix. The formation of NCs and beta-Sn segregation were discussed in relation to the deposition and processing conditions by employing HRTEM, XRD and Raman spectroscopy studies. The spectral photosensitivity exhibited up to 2000 nm in short-wavelength infrared (SWIR) depending on the Sn composition was obtained. Comparing to similar results on GeSn NCs in SiO2 matrix, the addition of Si offers a better thermal stability of SiGeSn NCs, while the use of HfO2 matrix results in better passivation of NCs increasing the SWIR photosensitivity at room temperature. These results suggest that SiGeSn NCs embedded in an HfO2 matrix are a promising material for SWIR optoelectronic devices.

This work describes the development of a flexible uric acid (UA) biosensor based on palladium-coated submicrometer electrospun poly(methylmethacrylate) (PMMA) fibers metalized with gold and attached to polyethylene terephthalate substrate (Pd/Au/PMMA/PET). The morphological characterization conducted by scanning electron microscopy revealed nanoscale Pd dendritic structures. Electrochemical investigations in the absence and in the presence of redox probes demonstrated that these Pd nanostructures are responsible for a six-fold increase in the electroactive area and enhanced electron transfer kinetics when compared to the gold-coated electrospun fibers. The UA biosensor obtained by immobilizing the uricase enzyme (UrOx) onto the Pd/Au/PMMA/PET electrode surface, allowed UA detection with a sensitivity of 431 mu A cm(-2) mM(-1) and a limit of detection of 12 mu M. Investigation of the redox reactions of hydrogen peroxide (a product of the enzymatic oxidation of UA by UrOx) at the Pd/Au/PMMA/PET electrode demonstrated that the working principle of the biosensor is based on the reduction of PdO produced at the electrode surface during the spontaneous reduction of hydrogen peroxide on Pd. This allows a biosensor operating potential of -0.05 V (vs Ag/AgCl) with high selectivity. The UrOx/Pd/Au/PMMA/PET biosensor was applied for UA detection in body fluids (sweat, urine, and blood serum) with recovery values between 98 and 105%, which were validated by high-performance liquid chromatography analysis. The stability of the device was evaluated over a period of 3 months, retaining 78% of the initial sensitivity, and reproducibility with RSD = 4.9% was achieved. The analytical performance of the biosensor under harsh mechanical deformations and at physiological temperatures demonstrated the potential applications of the device to wearable sensing platforms.

Quantum electrodynamical density functional theory is applied to obtain the electronic density, spin polarization, as well as orbital and spin magnetizations of square periodic arrays of quantum dots or antidots subjected to the influence of a far-infrared cavity photon field. A gradient-based exchange-correlation functional adapted to a 2D electron gas in a transverse homogeneous magnetic field is used in the theoretical framework and calculations. The obtained results predict a non-trivial effect of the cavity field on the electron distribution in the unit cell of the superlattice, as well as on the orbital and spin magnetizations. The number of electrons per unit cell of the superlattice is shown to play a crucial role in the modification of the magnetization via the electron-photon coupling. The calculations show that cavity photons strengthen the diamagnetic effect in the quantum dot structure, while they weaken the paramagnetic effect in the antidot structure. As the number of electrons per unit cell of the lattice increases, the electron-photon interaction reduces the exchange forces that will otherwise promote strong spin splitting for both the dot and the antidot arrays. Electronic density, spin polarization, as well as orbital and spin magnetizations of square periodic arrays of quantum dots or antidots subjected to the influence of a far-infrared cavity photon field are obtained using quantum electrodynamical density functional theory adapted to a 2D electron gas in a transverse homogeneous magnetic field. image

This paper tackles the influence of the functionalization of polystyrene and graphene oxide (GO) composites on the flammability characteristics. A microscale combustion calorimeter (MCC) was used to experimentally determine the heat release capacity (HRC), the specific heat release rate (HRR) and the total heat released (THR). Neural models were designed that correlate the THR with a number of parameters related to the composition and type of flame retardant used, the heating rate, the amount of residue, the HRC, the peak heat release rate (PHRR), the temperature at the peak pyrolysis rate (TPHRR) and the time elapsed until the occurrence of the peak heat release rate (Time). The best results in the training, validation and testing stages were achieved with the neural model with 9 neurons in the input layer, 40 neurons in the hidden layer and one neuron in the output layer. This model was incorporated into an optimization procedure, based on a genetic algorithm, to establish the values of the input parameters used in the training of the neural networks, in order to generate a minimum THR value, which is the output parameter. Since the synthesis of polystyrene particles with different GO concentrations is costly, this research helps to reduce the number of experimental tests and allows to determine the best GO concentration by means of neural models and genetic algorithms.

The bioavailability of the administered drugs that reach the systemic circulation is the first point in resolving the pathology of patients. Albumin-based nanoparticles represent an increasingly used strategy to deliver cancer drugs into cells that otherwise cannot overcome biological barriers. In this work, rutin (Ru), a flavonoid with anticancer and antioxidant potential, was incorporated into bovine serum albumin nanoparticles (BSA-Ru NPs), developed using the desolvation method, and the entire system was characterized and evaluated by scanning electron microscopy (SEM), atomic force microscopy (AFM), and UV-Vis absorption spectroscopy. The results showed that BSA and BSA-Ru NPs are uniformly distributed, have relatively large sizes, and have a time stability of more than 60%. Furthermore, the effect of these nanohybrids on the thermal stability of liposomal membranes was evaluated by surface plasmon resonance (SPR), cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). The viability evaluation was assessed by the tetrazolium salt (3-(4,5-dimethylthiazol-2-yl)-5-(3-carboxymethoxyphenyl)-2-(4-sulfophenyl)-2H-tetrazolium) (MTS) protocol in the fibroblast L929 line and a high level of biocompatibility, confirmed by SEM results, was found.

This study investigates the morphological changes induced by femtosecond (fs) laser pulses in arsenic trisulfide (As2S3) thin films and gold-arsenic trisulfide (Au\As2S3) heterostructures, grown by pulsed laser deposition (PLD). By means of a direct laser writing experimental setup, the films were systematically irradiated at various laser power and irradiation times to observe their effects on surface modifications. AFM was employed for morphological and topological characterization. Our results reveal a clear transition threshold between photoexpansion and photoevaporation phenomena under different femtosecond laser power regimes, occurring between 1 and 1.5 mW, irrespective of exposure time. Notably, the presence of a gold layer in the heterostructure minimally influenced this threshold. A maximum photoexpansion of 5.2% was obtained in As2S3 films, while the Au\As2S3 heterostructure exhibited a peak photoexpansion of 0.8%. The study also includes a comparative analysis of continuous-wave (cw) laser irradiation, confirming the efficiency of fs laser pulses in inducing photoexpansion effects.